ASTALAC™ ABS KMS
丙烯腈丁二烯苯乙烯
Marplex Australia Pty. Ltd.
Technical Data
產品說明
ASTALAC™ ABS KMS was upgraded in November 2007 to comply with RoHS and is a high impact strength flame retardant grade of ABS designed for sheet extrusion applications requiring flame retardancy, superior toughness and abuse resistance whilst maintaining a balance of high gloss, easy formability and product rigidity. Typical thermoformed applications include large air conditioner/heater unit casings and advertising signage blanks.
Note: The letters "UV" or "W" indicate UV stabilisation has been added [ ie: ASTALAC™ ABS KMSUV ].
總體
材料狀態 • 已商用：當前有效
資料 1 • Technical Datasheet (English)
搜索 UL 黃卡 • Marplex Australia Pty. Ltd.
• ASTALAC™
供貨地區 • 北美洲 • 南美洲 • 亞太地區
添加劑 • 阻燃
性能特點 • 光澤，高 • 韌性良好 • 阻燃性能
• 抗撞擊性，高 • 中等硬度
用途 • 片材
RoHS 合規性 • RoHS 合規
加工方法 • 片材擠出成型 • 熱成型
物理性能 額定值單位制 測試方法
比重 1.15g/cm³ ASTM D792
熔流率 (230°C/3.8 kg) 1.5g/10 min ASTM D1238
收縮率 - 流動 (3.00 mm) 0.40 到 0.80% ASTM D955
吸水率 (24 hr) 0.25% ASTM D570
機械性能 額定值單位制 測試方法
抗張強度 3 (3.20 mm) 36.0MPa ASTM D638
伸長率 3 (斷裂, 3.20 mm) 50% ASTM D638
彎曲模量 4 (3.20 mm) 2050MPa ASTM D790
彎曲強度 4 (3.20 mm) 62.0MPa ASTM D790
沖擊性能 額定值單位制 測試方法
懸壁梁缺口沖擊強度 (3.20 mm) 400J/m ASTM D256
落錘沖擊 (3.20 mm) 40.0J ASTM D3029
硬度 額定值單位制 測試方法
洛氏硬度 (R 計秤) 86 ASTM D785
熱性能 額定值單位制 測試方法
熱變形溫度 ASTM D648
1.8 MPa, 未退火, 3.20 mm 72.0°C
1.8 MPa, 未退火, 12.7 mm 84.0°C
維卡軟化溫度 98.0°C ASTM D1525 5
線形膨脹系數 - 流動 0.000090cm/cm/°C ASTM D696
可燃性 額定值單位制 測試方法
熱燈絲點火溫度 (1.60 mm) 960°C AS/NZS 60695
擠出 額定值單位制
干燥溫度 85.0 到 90.0°C
干燥時間 3.0 到 5.0hr
第1氣缸區溫度 170 到 190°C
第2氣缸區溫度 175 到 200°C
第3氣缸區溫度 180 到 205°C
第4氣缸區溫度 185 到 210°C
ASTALAC™ ABS KMS
丙烯腈丁二烯苯乙烯
Marplex Australia Pty. Ltd.
擠出 額定值單位制
第5氣缸區溫度 190 到 220°C
熔體溫度 190 到 230°C
模具溫度 180 到 220°C
牽引輥 75.0 到 105°C
背壓 10.0 到 25.0MPa
|